RES 12.4K OHM 1/16W 0.1% 0402SMD

RG1005P-1242-B-T5

Manufacturer Part NumberRG1005P-1242-B-T5
DescriptionRES 12.4K OHM 1/16W 0.1% 0402SMD
ManufacturerSusumu
SeriesRG
RG1005P-1242-B-T5 datasheet
 

Specifications of RG1005P-1242-B-T5

Resistance (ohms)12.4KPower (watts)0.063W, 1/16W
CompositionThin FilmTemperature Coefficient±25ppm/°C
Tolerance±0.1%Size / Dimension0.039" L x 0.020" W (1.00mm x 0.50mm)
Height0.014" (0.35mm)Lead StyleSurface Mount (SMD - SMT)
Package / Case0402 (1005 Metric)Resistance In Ohms12.4K
Case0402 (1005 metric)Resistance12.4 KOhms
Power Rating0.03 Watt (1/32 Watt)Voltage Rating25 Volts
Operating Temperature Range- 55 C to + 155 CTermination StyleSMD/SMT
Dimensions0.5 mm W x 1 mm L x 0.35 mm HProductPrecision Resistors Thin Film SMD
Lead Free Status / RoHS StatusLead free / RoHS CompliantFeatures-
Other namesRG10P12.4KBTR  
1
Page 1
2
Page 2
3
Page 3
4
Page 4
5
Page 5
6
Page 6
7
Page 7
8
Page 8
9
Page 9
10
Page 10
11
12
13
14
15
16
Page 9/16

Download datasheet (841Kb)Embed
PrevNext
Electrical Features Data
Excellent resistance stability (little secular distortion)
Through stable thin film forming processes and unique annealing treatment (aging), resistance
change is minimized durable resistor against environment in long term usage. Resistance change
is little even in high temperature and high humidity environment for long term.
■Thin Film (Susumu) vs Thick Film (Competitor)
●High Temperature Storage Test 155℃
0.5
Test Conditions
0.4
 Temperature 155℃ No load
 n=50
Sample
0.3
 1608 chip resistor
 RG1608=High Reliability
0.2
 Thick Film 1608 A Co., B Co.
0.1
0.0
−0.1
−0.2
−0.3
A Co. Thick Film 1608 (R=100kΩ)
B Co. Thick Film 1608 (R=100kΩ)
−0.4
RG1608-100kΩ
−0.5
10
100
Test Time (h)
Temperature Coefficient of Resistance (TCR)
Absolute TCR: ±2ppm/℃,
TCR ratio: ±1ppm/℃
●Metals have positive TCR and non or semi-
conductors have negative TCR. A thick film
resistor is normally a composite of metals
and
non-conductive
materials.
positive TCR when the resistance value is
high due to its high content of non-conductor
and negative TCR when resistance is low with
its high metal content. Our thin film resistor,
with
its
proprietary
composition
deposition method, shows close to zero TCR
regardless the resistance value.
(R−R
(R−R
0
−6
TCR (10
/K) =
×
R
0
where R : measured resistant value at t℃ (Ω)
R
: measured resistant value at t
0
t : measured test temperature (℃)
t
: measured standard temperature (℃)
0
●Temperature Humidity Bias (THB) 85℃ 85%
1.5
Test Conditions
 Temp. 85℃ Humidity 85%RH
 1/10 of rated power continuous load
1.0
 n=100
Sample
 1608 chip resistor
 RG1608=High Reliability
0.5
 Thick Film1608 A Co., B Co.
0.0
−0.5
−1.0
A Co. Thick Film 1608 (R=100kΩ)
B Co. Thick Film 1608 (R=100kΩ)
RG1608-100kΩ
−1.5
1000
10000
10
●Temperature Coefficient of Resistance
 −Thin Film (Susumu) vs Thick Film (Competitor)−
150
100
It
shows
50
0
−50
−100
and
−150
10Ω
SSM Thin Film RG1005
0
6
×10
t−t
0
℃ (Ω)
0
Reliability test 10,000Hr<0.1%
Electrical Features Data
100
1000
Test Time (h)
Sample: 1005 (inch 0402 size) Chip RES
1kΩ
10kΩ
100kΩ
10Ω
1kΩ
10kΩ
Thick Film 1005 Clip RES
Resistance Value, Type
10000
100kΩ
9