GRM21BR71H105MA12L Murata Electronics North America, GRM21BR71H105MA12L Datasheet - Page 77

• Manufacturer Part Number: GRM21BR71H105MA12L
• Description: CAP CER X7R 0805
• Manufacturer: Murata Electronics North America
• Series: GRMr

Specifications of GRM21BR71H105MA12L

• Voltage - Rated: 50V
• Lead Style: *
• Capacitance: 1.0µF
• Tolerance: ±20%
• Temperature Coefficient: X7R
• Mounting Type: *
• Operating Temperature: -55°C ~ 125°C
• Applications: General Purpose
• Package / Case: *
• Size / Dimension: *
• Thickness: *
• Lead Spacing: *
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant
• Features: -
• Ratings: -

!Note
• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our
• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
sales representatives or product engineers before ordering.
!Note
!Note
No.
12 Deflection
13
14
15
16
17 Durability
GNM Series Specifications and Test Methods (2)
Continued from the preceding page.
Solderability of
Termination
Resistance
to Soldering
Heat
Temperature
Cycle
High
Temperature
High
Humidity
(Steady)
1. This Specifications and Test Methods is downloaded from the website of Murata Manufacturing co.,ltd. Therefore, it's specifications are subject to change or our products in it may be discontinued without advance notice.
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
0.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
2. This Specifications and Test Methods has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product
0.
Please check with our sales representatives or product engineers before ordering.
specifications before ordering.
Item
Appearance No marking defects
Capacitance
Change
Appearance No marking defects
Capacitance
Change
D.F.
I.R.
Dielectric
Strength
Appearance No marking defects
Capacitance
Change
D.F.
I.R.
Dielectric
Strength
Appearance No marking defects
Capacitance
Change
D.F.
I.R.
Appearance No marking defects
Capacitance
Change
D.F.
I.R.
Within 10%
75% of the terminations are to be soldered evenly
and continuously.
R6*
*
0.1 max. *
*
50 · F min.
No failure
R6*
*
0.1 max. *
*
50 · F min.
No failure
R6: Within 12.5%
0.2 max.
12.5 · F min.
R6: Within 12.5%
0.2 max.
25 · F min.
4
3
5
3
GNM0M2R60G105: Within +15/-7.5%
However 0.125 max. for Table 3 items.
GNM0M2R60G105, GNM0M2R60J103/223/473/104,
GNM0M2R61A103/223/473/104,
GNM0M2R61C103/223/473/104, GNM1M2R61A105:
However 0.125 max. for Table 3 items.
4
5
: Within 7.5%
: Within 12.5%
GNM0M2
GNM1M2
GNM212
GNM214
GNM314
#GNMpp4
Type
3
3
5.0
d
a
b
c
100
1.0
2.0 0.05
2.0 0.05
2.0 0.05
2.0 0.05
2.5 0.05
a
When no "*" is added in PNs table, please refer to GNM Series Specifications and Test Methods (1).
Specifications
When "*" is added in PNs table, please refer to GNM Series Specifications and Test Methods (2).
Fig. 2
0.2 0.05
0.5 0.05
0.6 0.05
0.7 0.05
0.8 0.05
#GNMpp2
b
GNM Series Specifications and Test Methods (2)
5.0
d
a
b
c
0.32 0.05
0.2 0.05
0.5 0.05
0.3 0.05
0.4 0.05
100
1.0
c
Thickness: 0.8mm
Within 15%
0.25 0.05
0.32 0.05
0.5 0.05
0.2 0.05
0.4 0.05
(in mm)
d
Solder the capacitor to the test jig (glass epoxy board) shown in
Fig. 2 using a eutectic solder. Then apply a force in the
direction shown in Fig. 3. The soldering should be done by the
reflow method and should be conducted with care so that the
soldering is uniform and free of defects such as heat shock.
Immerse the capacitor in a solution of ethanol (JIS-K-8101) and
rosin (JIS-K-5902) (25% rosin in weight proportion). Preheat at
80 to 120 C for 10 to 30 seconds. After preheating, immerse in
eutectic solder solution for 2 0.5 seconds at 230 5 C or
Sn-3.0Ag-0.5Cu solder solution for 2 0.5 seconds at 245 5 C.
Preheat the capacitor at 120 to 150 C for 1 minute. Immerse
the capacitor in a eutectic solder or Sn-3.0Ag-0.5Cu solder
solution at 270 5 C for 10 0.5 seconds.
Let sit at room temperature for 24 2 hours, then measure.
• Initial measurement
Fix the capacitor to the supporting jig in the same manner and
under the same conditions as (10).
Perform the five cycles according to the four heat treatments
listed in the following table.
Let sit for 24 2 hours at room temperature, then measure.
• Initial measurement
Apply the rated voltage at 40 2 C and 90 to 95% humidity for
500 12 hours. The charge/discharge current is less than 50mA.
• Initial measurement
• Measurement after test
Apply 150% (GNM1M2R61A225/1C105: 125% of the rated
voltage) of the rated voltage for 1000 12 hours at the
maximum operating temperature 3 C. Let sit for 24 2 hours
at room temperature, then measure.
The charge/discharge current is less than 50mA.
• Initial measurement
• Measurement after test
Perform a heat treatment at 150 +0/-10 C for one hour and
then let sit for 24 2 hours at room temperature. Perform
the initial measurement.
Perform a heat treatment at 150 +0/-10 C for one hour and
then let sit for 24 2 hours at room temperature.
Perform the initial measurement.
Perform a heat treatment at 150 +0/-10 C for one hour
and then let sit for 24 2 hours at room temperature.
Perform the initial measurement.
Perform a heat treatment at 150 +0/-10 C for one hour
and then let sit for 24 2 hours at room temperature, then
measure.
Perform a heat treatment at 150 +0/-10 C for one hour
and then let sit for 24 2 hours at room temperature.
Perform the initial measurement.
Perform a heat treatment at 150 +0/-10 C for one hour and
then let sit for 24 2 hours at room temperature, then measure.
Temp. ( C)
Time (min.)
Step
Min. Operating
Temp.
R230
30 3
1
Capacitance meter
45
Fig. 3
Test Method
20
Temp.
Room
2 to 3
50
Pressurize
45
2
Pressurizing
speed: 1.0mm/sec.
Min. Operating
Flexure : V1
Temp.
30 3
3
Temp.
Room
2 to 3
4
75
C02E.pdf
10.12.20