B72220S251K101 EPCOS Inc, B72220S251K101 Datasheet - Page 19

• Manufacturer Part Number: B72220S251K101
• Description: Varistor, Circuit Protection; 250Vrms; 650V; 8000A; Metal Oxide; 700pF; Wire; 1W; 25ns
• Manufacturer: EPCOS Inc
• Type: MOVr

Specifications of B72220S251K101

• Technology: Metal Oxide
• Capacitance Value: 700pF
• Clamping Current: 100A
• Clamping Voltage: 650V
• Lead Style: Radial
• Ac Voltage Rating (max): 250VAC
• Dc Voltage Rating (max): 320VDC
• Operating Temp Range: -40C to 85C
• Mounting: Through Hole
• Surge Current (max): 8000A
• Lead Spacing: 10mm
• Product Depth (mm): 5.3mm
• Product Height (mm): 25.5mm
• Product Diameter (mm): 21.5mm
• Energy: 140Joule
• Varistor Voltage: 390V
• Brand/series: Standard Series
• Capacitance: 700 pF
• Current, Peak: 8000 A
• Current, Surge: 8000 A
• Dimensions: 21.5 mm (Max.) Dia. x 5.3 mm (Max.) W x 25.5 mm (Max.) H
• Electric Strength: ≥2.5 kV (RMS) (Min.)
• Energy Rating: 130 Joules
• Mounting Style: Leaded
• Package: Leads
• Power Rating: 1.00 W (Max.) @ +85 °C
• Resistance, Insulation: ≥10 Megohms (Min.)
• Temperature, Operating, Maximum: 85 °C
• Temperature, Operating, Minimum: -40 °C
• Terminal Type: Tinned Copper
• Voltage, Ac: 250 VAC
• Voltage, Clamping: 650 V
• Voltage, Dc: 320 VDC
• Voltage, Operating: 250 Vrms @ +85 °C, 320 VDC @ +85 °C
• Voltage, Varistor: 390
• Lead Free Status / RoHS Status: Compliant

Reliability data
Test
Climatic sequence
Fast temperature cycling
Damp heat, steady state
Solderability
Please read Cautions and warnings and
Important notes at the end of this document.
Test methods/conditions
CECC 42 000, test 4.16
The specimen shall be subjected to:
a) dry heat at UCT, 16 h
b) damp heat, 1st cycle:
c) cold, LCT, 2 h
d) damp heat, additional 5 cycles:
Then the specimen shall be stored at
room temperature and normal humidity
for 1 to 2 h.
Thereafter, the change of V
measured. Thereafter, insulation resis-
tance R
to CECC 42 000, test 4.8 at V = 500 V.
IEC 60068-2-14, test Na, LCT/UCT,
dwell time 30 min, 5 cycles
The specimen shall be subjected to
40 ±2 °C, 90 to 95% r. H. for 56 days
without load / with 10% of the maximum
continuous DC operating voltage V
Then stored at room temperature and
normal humidity for 1 to 2 h.
Thereafter, the change of V
measured. Thereafter, insulation resis-
tance R
to CECC 42 000, test 4.8 at V = 500 V.
IEC 60068-2-20, test Ta,
method 1 with modified conditions for
lead-free solder alloys: 245 °C, 3 s:
After dipping the terminals to a depth
of approximately 3 mm from the body
in a soldering bath of 245 °C for 3 s, the
terminals shall be visually examined.
55 °C, 93% r. H., 24 h
55 °C/25 °C, 93% r. H., 24 h/cycle.
ins
ins
shall be measured according
shall be measured according
19
11/07
v
v
shall be
shall be
Leaded varistors
StandarD series
DC
.
Requirement
|
R
|
No visible damage
|
R
The inspection shall be
carried out under adequate
light with normal eyesight or
with the assistance of a
magnifier capable of giving
a magnification of 4 to
10 times. The dipped sur-
face shall be covered with
a smooth and bright solder
coating with no more than
small amounts of scattered
imperfections such as
pinholes or un-wetted or
de-wetted areas. These
imperfections shall not be
concentrated in one area.
∆V/V (1 mA)
∆V/V (1 mA)
∆V/V (1 mA)
ins
ins
≥1 MΩ
≥1 MΩ
|
|
|
≤10%
≤5%
≤10%