CL21B103KCANNNC SAMSUNG, CL21B103KCANNNC Datasheet - Page 8

• Manufacturer Part Number: CL21B103KCANNNC
• Description: MLCC 0805 X5R 10NF 10% 100V
• Manufacturer: SAMSUNG
• Series: CLr

Specifications of CL21B103KCANNNC

• Size: 0905
• Dielectric: X7R
• Tolerance: +/- 10%
• Voltage: 100V
• Thickness: 0.65
• Electrode/termination/platin: Ni/Cu/Sn 100%
• Products: Normal

NO
10
11
12
RELIABILTY TEST CONDITION
Soldering heat
Resistance to
Vibration
Test
Solder ability
ITEM
Withstanding
Capacitance
Appearance
Capacitance
Apperance
Resistance
Resistance
(Class Ⅰ)
(Class Ⅱ)
(Class Ⅰ)
(Class Ⅱ)
Insulation
Insulation
Voltage
Tanδ
Tanδ
Q
Q
More Than 75% of the terminal surface is to
be soldered newly, So metal part does not
come out or dissolve
No mechanical damage shall occur.
Class Ⅱ
Capacitance ≥ 30㎊
Within the specified initial value
Within the specified initial value
Within the specified initial value
No mechanical damage shall occur.
Within the specified initial value
Within the specified initial value
Within the specified initial value
Class
Characteristics
Characteristics
Ⅱ
Class Ⅰ
Class Ⅰ
A(X5R)/
A(X5R)/
B(X7R)
X(X6S)
B(X7R)
X(X6S)
F(Y5V)
<30㎊
PERFORMANCE
F
Within ±2.5% or
±0.25㎊ whichever is
larger
Within ±7.5%
Within ±15%
Within ±20%
Within ±2.5% or
±0.25㎊ whichever is
larger
Within ±5%
Within ±10%
Within ±20%
: Q≥ 1000
: Q≥ 400+20×C
Capacitance Change
Capacitance Change
(C: Capacitance)
Solder Temperature : 270±5℃
Dip Time : 10±1 sec.
Each termination shall be fully immersed and
preheated as below :
Leave the capacitor in ambient condition for
specified time* before measurement
* 24 ± 2 hours (Class Ⅰ)
The capacitor shall be subjected to a
Harmonic Motion having a total amplitude of
1.5mm changing frequency from 10Hz to 55Hz
and back to 10Hz In 1 min.
Repeat this for 2hours each in 3 mutually
perpendicular directions
Pre-heating
Dip Time
STEP
24 ± 2 hours (Class Ⅱ)
Solder
Solder
Temp.
Flux
1
2
TEMP.(℃)
150~180
TEST CONDITION
80~100
Sn-3Ag-0.5Cu
at 80~120℃ for 10~30 sec.
3±0.3 sec.
245±5℃
RMA Type
TIME(SEC.)
63Sn-37Pb
5±0.5 sec.
60
60
235±5℃