GRM31CR61E226KE15L Murata, GRM31CR61E226KE15L Datasheet - Page 60

• Manufacturer Part Number: GRM31CR61E226KE15L
• Description: Multilayer Ceramic Capacitors (MLCC) - SMD/SMT 1206 X5R 25V 22uF
• Manufacturer: Murata
• Series: GRMr

Specifications of GRM31CR61E226KE15L

• Voltage Rating: 25 Volts
• Operating Temperature Range: - 55 C to + 85 C
• Temperature Coefficient / Code: X5R
• Product: Automotive MLCCs
• Dimensions: 1.6 mm W x 3.2 mm L x 1.6 mm H
• Termination Style: SMD/SMT
• Capacitance: 22 uF
• Tolerance: 10 %
• Package / Case: 1206 (3216 metric)
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant

!Note
• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our
• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
sales representatives or product engineers before ordering.
!Note
58
No.
10
11 Vibration
GRM Series Specifications and Test Methods (2) (Note 1)-Typical Inspection
9
Continued from the preceding page.
Capacitance
Temperature
Characteristics
Adhesive Strength
of Termination
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
GRM Series Specifications and Test Methods (2) (Note 1)-Typical Inspection
Item
No bias
50% of
the Rated
Voltage
Appearance
Capacitance
D.F.
B1, B3 : Within 10% (–25 to +85 C)
F1
R6
R1, R7 : Within 15% (–55 to +125 C)
F5
C6
C7
C8
D7
E7
D8
B1: Within +10/–30%
R1: Within +15/–40%
F1: Within +30/–95%
No removal of the terminations or other defects should occur.
No defects or abnormalities
Within the specified tolerance
B1, B3, R1, *R6, *R7, C7, C8, E7, D7: 0.1 max.
C6: 0.125 max.
D8: 0.15 max.
F1, F5: 0.2 max.
*GRM31CR71E106: 0.125 max.
GRM31CR6 0J/0G 107: 0.15 max.
: Within +30/–80% (–25 to +85 C)
: Within 15% (–55 to +85 C)
: Within +22/–82% (–30 to +85 C)
: Within 22% (–55 to +85 C)
: Within 22% (–55 to +125 C)
: Within 22% (–55 to +105 C)
: Within +22/–33% (–55 to +125 C)
: Within +22/–56% (–55 to +125 C)
: Within +22/–33% (–55 to +105 C)
When no "*" is added in PNs table, please refer to GRM Series Specifications and Test Methods (1).
Specifications
When "*" is added in PNs table, please refer to GRM Series Specifications and Test Methods (2).
Fig. 1a
Please refer to individual specifications (our product specifications or the approval sheet).
c
Solder resist
Baked electrode or
copper foil
(Note 1) These Specifications and Test Methods indicate typical inspection.
The capacitance change should be measured after 5 min. at
each specified temp. stage.
The ranges of capacitance change compared with the
reference temperature value over the temperature ranges
shown in the table should be within the specified ranges.*
In case of applying voltage, the capacitance change should be
measured after 1 more min. with applying voltage in
equilibration of each temp. stage.
*GRM32DR60J226, GRM43 B1/B3/R6 0J/1A 336/476: 1.0 0.2Vrms
•Initial measurement for high dielectric constant type
Perform a heat treatment at 150 +0/–10 C for one hour and
then set for 24 2 hours at room temperature.
Perform the initial measurement.
Solder the capacitor on the test jig (glass epoxy board) shown
in Fig. 1a using a eutectic solder. Then apply 10N* force in
parallel with the test jig for 10 1sec.
The soldering should be done either with an iron or using the
reflow method and should be conducted with care so that the
soldering is uniform and free of defects such as heat shock.
*1N: GRM02, 2N: GRM03, 5N: GRM15/GRM18
Solder the capacitor on the test jig (glass epoxy board) in the
same manner and under the same conditions as (10).
The capacitor should be subjected to a simple harmonic motion
having a total amplitude of 1.5mm, the frequency being varied
uniformly between the approximate limits of 10 and 55Hz. The
frequency range, from 10 to 55Hz and return to 10Hz, should
be traversed in approximately 1 minute. This motion should be
applied for a period of 2 hours in each of 3 mutually
perpendicular directions (total of 6 hours).
GRM155B30G475, GRM155B30J 225, GRM21BB30J476,
GRM155R60E106, GRM188 B3/R6 0E/0G/0J 226: 0.2 0.05Vrms
Step
GRM02
GRM03
GRM15
GRM18
GRM21
GRM31
GRM32
GRM43
GRM55
1
2
3
4
5
6
7
8
25 2 (for R6, R7, C6, C7, C8, D7, D8, E7, F5)
20 2 (for B1, B3, F1, R1)
–55 3 (for R1, R6, R7, C6, C7, C8, D7, D8, E7)
–30 3 (for F5)
–25 3 (for B1, B3, F1)
25 2 (for R6, R7, C6, C7, C8, D7, D8, E7, F5)
20 2 (for B1, B3, F1, R1)
125 3 (for R1, R7, C7, D7, E7)
105 3 (for C8, D8)
85 3 (for B1, B3, F1, F5, R6, C6)
20 2 (for B1, F1, R1)
–55 3 (for R1)
–25 3 (for B1, F1)
20 2 (for B1, F1, R1)
125 3 (for R1)
85 3 (for B1, F1)
Type
Temperature ( C)
0.2
0.3
0.4
1.0
1.2
2.2
2.2
3.5
4.5
Test Method
a
Continued on the following page.
0.56
0.9
1.5
3.0
4.0
5.0
5.0
7.0
8.0
b
Applying Voltage (V)
rated voltage
50% of the
No bias
0.23
1.65
0.3
0.5
1.2
2.0
2.9
3.7
5.6
c
C02E.pdf
10.12.20