CC0805KKX7R0BN152 Yageo, CC0805KKX7R0BN152 Datasheet - Page 14

CAP CERAMIC 1500PF 100V 0805 X7R

CC0805KKX7R0BN152

Manufacturer Part Number
CC0805KKX7R0BN152
Description
CAP CERAMIC 1500PF 100V 0805 X7R
Manufacturer
Yageo
Series
CCr
Datasheet

Specifications of CC0805KKX7R0BN152

Capacitance
1500pF
Voltage - Rated
100V
Tolerance
±10%
Temperature Coefficient
X7R
Mounting Type
Surface Mount, MLCC
Operating Temperature
-55°C ~ 125°C
Applications
General Purpose
Package / Case
0805 (2012 Metric)
Size / Dimension
0.079" L x 0.049" W (2.00mm x 1.25mm)
Thickness
0.85mm
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Features
-
Ratings
-
Lead Spacing
-
Other names
08052R152K0BB00
Q1131860F
Sep 08, 2005 V.0
TEST
Bond strength
soldering heat
Resistance to
Rapid change
temperature
of plating on
with U
Table 10 Test condition, procedure and requirements (continued)
Solderability
Damp heat,
end face
r
load
of
Surface-Mount Ceramic Multilayer Capacitors
TEST METHOD
IEC 60384-
21/22
4.8
4.9
4.10
4.11
4.13
PROCEDURE
Precondition: 150 +0/–10 °C for 1 hour, then keep for
24 ±1 hours at room temperature
Preheating: for size ≤ 1206: 120 to 150 °C for 1 minute
Preheating: for size >1206: 100 to 120 °C for 1 minute
and 170 to 200 °C for 1 minute
Solder bath temperature: 260 ±5 °C
Dipping time: 10 ±0.5 seconds
Recovery time: 24 ±2 hours.
Unmounted chips completely immersed in a solder bath
at 235 ±5 °C
Dipping time: 2 ±0.5 seconds
Depth of immersion: 10 mm
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for 24 ±1 hours at
room temperature
5 cycles with following detail:
30 minutes at lower category temperature;
30 minutes at upper category temperature
Recovery time 24 ±2 hours.
Initial measurements; after 150 +0/-10 °C for 1 hour,
then keep for 24 ±1 hours at room temperature
Duration and conditions: 500 ±12 hours at 40 ±2 °C;
90 to 95% RH; U
Final measurement: perform a heat treatment at
150 +0/–10 °C for 1 hour, final measurements shall be
carried out 24 ±1 hours after recovery at room
temperature without load.
Mounting in accordance with IEC 60384-22 paragraph
4.3
Conditions: bending 1 mm at a rate of 1 mm/s, radius jig
340 mm
r
applied
Mid-voltage
NP0
/
X7R
REQUIREMENTS
No visible damage
NP0: l∆C/Cl: ≤ 1% or 0.5 pF
whichever is greater
X7R: l∆C/Cl: ≤ 10%
The termination shall be well tinned
NP0: l∆C/Cl: ≤ 0.5% or 0.5 pF
whichever is greater
X7R: l∆C/Cl: ≤ 10%
D.F.: within initial specified value
R
The termination shall be well
tinned.
No visual damage
NP0: l∆C/Cl: ≤ 1% or 1 pF
whichever is greater
X7R: l∆C/Cl: ≤ 15%
D.F.: within initial specified value
R
NP0: l∆C/Cl: ≤ 2% or 1 pF
whichever is greater
X7R: l∆C/Cl: ≤ 15%
NP0: D.F.: 2 × initial value max.
X7R ≥ 100 V: D.F. ≤ 5%
NP0: R
≥ 25 seconds, whichever is less
X7R: R
25 seconds, whichever is less
ins
ins
: within initial specified value
: within initial specified value
100 V to 500 V
ins
ins
≥ 500 MΩ or R
≥ 2,500 MΩ or R
Product specification
www.yageo.com
ins
ins
× C
× C
14
r
16
r