C5750X7R1E156MT5 TDK Corporation, C5750X7R1E156MT5 Datasheet - Page 10
![CAP CER 15UF 25V X7R 20% 2220](/photos/29/20/292011/c5750_series_sml.jpg)
C5750X7R1E156MT5
Manufacturer Part Number
C5750X7R1E156MT5
Description
CAP CER 15UF 25V X7R 20% 2220
Manufacturer
TDK Corporation
Series
Cr
Specifications of C5750X7R1E156MT5
Capacitance
15µF
Tolerance
±20%
Package / Case
2220 (5750 Metric)
Voltage - Rated
25V
Temperature Coefficient
X7R
Mounting Type
Surface Mount, MLCC
Operating Temperature
-55°C ~ 125°C
Features
Low ESR
Applications
General Purpose
Size / Dimension
0.224" L x 0.197" W (5.70mm x 5.00mm)
Thickness
2.80mm
Voltage Rating
25 Volts
Operating Temperature Range
- 55 C to + 125 C
Temperature Coefficient / Code
X7R
Product
Open Mode/Fail-Safe MLCC
Dimensions
5 mm W x 5.7 mm L x 2.3 mm H
Termination Style
SMD/SMT
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Ratings
-
Lead Spacing
-
Lead Free Status / Rohs Status
Lead free / RoHS Compliant
Other names
445-6120-2
• All specifications are subject to change without notice. Please read the precautions before using the product.
US Catalog // C Series — Open Mode Design // Version A11
No.
9
10
11
General
Specifications
Item
Solderability
Resistance to solder heat
External
appearance
Capacitance
D.F. (Class 2)
Insulation
Resistance
Voltage
Proof
Vibration
External
appearance
Capacitance
D.F. (Class 2)
Performance
New solder to cover over 75% of
termination.
25% may have pinholes or rough spots
but not concentrated in one spot.
Ceramic surface of “A sections” shall
not be exposed due to melting or
shifting of termination material.
No cracks are allowed and terminations
shall be covered at least 60% with new
solder.
Meet the initial spec.
Meet the initial spec.
No insulation breakdown or other
damage.
No mechanical damage.
Meet the initial spec.
Characteristics
Class 2
Characteristics
Class 2
X7R
X8R
X7R
X8R
A section
Change from the
value before test
± 7.5%
Change from the
value before test
± 7.5%
C Series — Open Mode Design
Test or Inspection Method
Completely soak both terminations in solder at
235±5ºC for 2±0.5s.
Solder: H63A (JIS Z 3282)
Flux: Isopropyl alcohol (JIS K 8839)
Completely soak both terminations in solder at
260±5ºC for 5±1s.
Preheating condition
Flux: Isopropyl alcohol (JIS K 8839)
Solder: H63A (JIS Z 3282)
Leave the capacitor in ambient conditions for 6 to 24h
before measurement.
Reflow solder the capacitor on P.C. board (shown in
Appendix 1a or Appendix 1b) before testing.
Vibrate the capacitor with amplitude of 1.5mm P-P
sweeping the frequencies from 10Hz to 55Hz and back
to 10Hz after 1min.
Repeat this for 2h each in 3 perpendicular directions.
Temp.: 150±10ºC
Time : 1 to 2min.
Rosin (JIS K 5902) 25% solid solution.
Rosin (JIS K 5902) 25% solid solution.