2108-P Techspray, 2108-P Datasheet - Page 2
![Chemicals CONFORMAL COATING 1 PINT GLASS BOTTLE](/photos/18/10/181085/2108-p_hi-res_sml.jpg)
2108-P
Manufacturer Part Number
2108-P
Description
Chemicals CONFORMAL COATING 1 PINT GLASS BOTTLE
Manufacturer
Techspray
Type
Conformalr
Datasheet
1.2108-P.pdf
(5 pages)
Specifications of 2108-P
Product
Coating Products
Chemical Component
Acetone/Acrylic Polymer/N-Heptane/N-Propyl Acetate
Dispensing Method
Bottle
Primary Type
Coating
Special Features
Repair/Service
Time, Setting
3 min.
Weight
1 Pint
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Cure Profile
Test Data
Application
2
Characteristics
Application Method
Cure time
Accelerated cure time
Dry time to touch
Quality inspection method of coverage
Removal method
As Supplied:
Visual appearance
Density (25 C)
Viscosity (25 C)
Solids %
Flash point
Vapor pressure (20 C) (VOC composite)
Initial boiling point
Stability (30‐day test @ 37 C/100 F)
Stability (30‐day test @ 6.1 C/21 F)
Resin T
Resin mol wt
g
Accelerated Cure:
Ambient Cure:
Tack-Time (dry to touch): 3 minutes @ 74°F / 23°C (ambient temp)
Cure time depends on a number of factors, including the method and thickness of
application. Dilution will also change the cure profile. 149°F / 65°C is recommended as
the best accelerated temperature to optimize leveling, providing the smoothest possible
finish. A faster cure may be achieved, but should be thoroughly tested first.
Test Method*
TS‐053
TS‐054
TS‐055
Test Method
TS‐050
TS‐019‐1
Instrument (Brookefield RVT) guide
TS‐015
ASTM D‐56 (TAG CC)
calculated
TS‐051
TS‐052
TS‐052‐1
provided by supplier
provided by supplier
20 minutes @ 149°F / 65°C
15 hours @ 74°F / 23°C (ambient temp)
Alkane, Acetone or Acetate, Solder iron burn through
For Commercial Use Only
Copyright 2008 Techspray.
Spray system, dip, or brush
UV (long‐wave black) light
2108 Test Results
2108 Test Results
25 min @65 C
25.02mm Hg
39.4C (103F)
0.8603 g/ml
1.7 C (35 F)
50 – 55 C
24 hours
15.70%
60,000
Stable
Stable
20 cp
3 min
Clear