0382-3-17-01-34-27-02-0 Mill-Max Manufacturing Corp., 0382-3-17-01-34-27-02-0 Datasheet - Page 3

• Manufacturer Part Number: 0382-3-17-01-34-27-02-0
• Description: RECEPT WRAPOST .032-.046" .089"
• Manufacturer: Mill-Max Manufacturing Corp.
• Type: Wire Wrapr
• Series: 0382r

Specifications of 0382-3-17-01-34-27-02-0

• Length: 0.763" (19.38mm)
• Inside Diameter: 0.064" (1.63mm)
• Hole Diameter: 0.089" (2.26mm)
• Flange Diameter: 0.120" (3.05mm)
• Mounting Type: Press Fit
• Contact Finish: Gold
• Contact Finish Thickness: 30µin (0.76µm)
• Number Of Contacts: 1POS
• Number Of Contact Rows: Not Required
• Row Spacing (mm): Not Requiredmm
• Pitch (mm): Not Requiredmm
• Grid Size: Not Required
• Contact Plating: Gold Over Nickel
• Mounting Style: Through Hole
• Contact Material: Beryllium Copper
• Operating Temp Range: -55C to 125C
• Product Depth (mm): 3.05mm
• Product Length (mm): 19.38mm
• Gender: RCP
• Body Orientation: Straight
• Current Rating: 8A
• Contact Resistance Max: 10mOhm
• Lead Free Status / RoHS Status: Not Compliant
• Other names: 0382-317013427020; 0382317013427020; 382317013427020

Mill-Max Mfg. Corp. Datasheet — Last Modified 12/11/2009
SHELL MATERIAL:
BRASS ALLOY
Properties of BRASS ALLOY:
Properties after heat treatment (TH01):
Hardness: 36-43 Rockwell C
Mechanical Life: 100 Cycles Min.
Density: .298 lbs/in3
Electrical Conductivity: 22% IACS*
Resistance: 10 miliohms Max
Operating Temperature: -55°C/+125°C
Melting point: 980°C/865°C (liquidus/solidus)
Stress Relaxation†: 96% of stress remains after
1,000 hours @ 100 °C ; 70% of stress remains after
1,000 hours @ 200 °C
*International Annealed Copper Standard, i.e. as a % of pure copper.
†Since BeCu loses its spring properties over time at high temperatures; it is rated for continuous use up to 150°C. For
applications up to 300°C, Mill-Max offers many contacts in Beryllium Nickel. Contact Tech Support for more info.
Chemical composition: Cu 61.5%, Zn 35.4%, Pb 3.1%†
Hardness as machined: 80-90 Rockwell B
Density: .307 lbs/in3
Electrical conductivity: 26% IACS*
Melting point: 900°C/885°C (liquidus/solidus)
†(3 to 4% lead is used to permit "free machining" and is permitted by EC Directive 2002/95Annex 6; so all pin materials
are RoHS compliant)
*International Annealed Copper Standard, i.e. as a % of pure copper.
(UNS C36000) per ASTM B 16