CA0612JRNPO9BN221 Yageo, CA0612JRNPO9BN221 Datasheet - Page 15

• Manufacturer Part Number: CA0612JRNPO9BN221
• Description: Family: C2 Type: CA Size: 0612 Tol: J Packing: R Material: NPO Volt: 9 Cap: 221 Actual Cap:220
• Manufacturer: Yageo

Jun 22, 2009 V.0
TEST
Rapid change
of
temperature
Damp heat
with U
r
load
Surface-Mount Ceramic Multilayer Capacitors
TEST METHOD
IEC 60384-
21/22
4.11
4.13
PROCEDURE
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for
24 ±1 hours at room temperature
5 cycles with following detail:
30 minutes at lower category temperature
30 minutes at upper category temperature
Recovery time 24 ±2 hours
1.
2.
3.
4.
5.
P.S. If the capacitance value is less than the
minimum value permitted, then after the
other measurements have been made the
capacitor shall be precondition according to
“IEC 60384 4.1” and then the requirement
shall be met.
Preconditioning, class 2 only:
150 +0/-10 °C /1 hour, then keep for
24 ±1 hour at room temp
Initial measure:
Spec: refer initial spec C, D, IR
Damp heat test:
500 ±12 hours at 40 ±2 °C;
90 to 95% R.H. 1.0 U
Recovery:
Class 1: 6 to 24 hours
Class 2: 24 ±2 hours
Final measure: C, D, IR
r
applied
4C-Array
REQUIREMENTS
No visual damage
<General purpose series>
∆C/C
Class 1:
NP0: within ±1% or 1 pF, whichever is greater
Class2:
X5R/X7R: ±15%
Y5V: ±20%
<High Capacitance series>
∆C/C
Class2:
X5R/X7R: ±15%
Y5V: ±20%
D.F. meet initial specified value
R
No visual damage after recovery
<General purpose series>
∆C/C
Class 1:
NP0: within ±2% or 1 pF, whichever is greater
Class2:
X5R/X7R: ±15%; Y5V: ±30%
D.F.
Class 1:
Class2:
X5R/X7R: ≤ 16V: ≤ 7%
Y5V: ≤ 15%
R
Class 1:
NP0: ≥ 2,500 MΩ or R
Class2:
X5R/X7R/Y5V: ≥ 500 MΩ or R
is less
<High Capacitance series>
∆C/C
Class2:
D.F.
Class2:
R
Class2:
ins
ins
ins
meet initial specified value
X5R/X7R: ±20%; Y5V: ±30%
2 x initial value max
500 MΩ or R
NP0: ≤ 2 x specified value
≥ 25V: ≤ 5%
NP0/X7R/Y5V
ins
ins
x C
x C
r
r
≥ 25s, whichever is less
≥ 25s whichever is less
16 V to 50 V
ins
Product specification
x C
r
www.yageo.com
≥ 25s whichever
15
17