Specifications of #4DFA-1575B-14=P
Maximum Insertion Loss
1.42 dB
■ PRECAUTIONS AND RECOMMENDED SOLDERING CONDITIONS FOR USING DIELECTRIC FILTERS
1. Reflow solder conditions
•Solderability
•Solder heat resistance
2. Rinsing
3. Other Precautions
4. Iron Soldering
SURFACE MOUNT TYPE
面実装誘電体フィルタご使用上の注意・推奨はんだ付け条件
When flux-mounted terminals are immersed in
solder at following conditions, at least 95% of the
surface should be covered by solder.
Conditins
leaded process : 215±5°C for 3±0.5 seconds
lead free process : 245±5°C for 3±0.5 seconds
No abnomalities under solder conditions of
leaded process : 230±5°C for 5 seconds
lead free process : 255±5°C for 5 seconds
After Soldering, you should rinsing away the
excess flux. Any commercially available rinsing
agent may be used.
Perform soldering at as low a temperature as
possible and for as short a time as possible.
Make sure that the silver electrode of resonators
is not covered by solder.
Avoid applying external forces to terminals such
as by bending or cutting them.
Perform iron soldering with iron at following
conditions.
Conditins
leaded process : 350°C for 5s. Max.
lead free process : 390±5°C for 5s. Max.
Dielectric Filters for Surface Mounting
面実装用誘電体フィルタ
1. リフローはんだ条件
2. 洗浄
3. その他留意事項
4. こてはんだ
・はんだ付け性
・はんだ耐熱性
フラックス付けした端子部を以下の条件ではんだ中に
浸漬し95%以上の面積がはんだで覆われること。
条件
有鉛品
鉛フリー品 : 245±5℃のはんだ中に3±0.5秒浸漬
以下のはんだ付け条件で異常のないこと。
有鉛品
鉛フリー品 : 255±5℃、5秒間
はんだ付け後のフラックスの洗浄をして下さい。
洗浄液として一般的に使用されている全ての洗浄液が
使用できます。
はんだ付けは極力低い温度で短時間で行って下さい。
共振器の銀電極にはんだが付着しないようにして下さ
い。
端子を曲げたり、切断するなど、端子部分に外力を加
えることは避けて下さい。
有鉛半田
無鉛半田
: 215±5℃のはんだ中に3±0.5秒浸漬
: 230±5℃、5秒間
: こて先温度350℃以下、加熱時間5秒
: こて先温度390±5℃、加熱時間5秒
以内、1回
以内、1回