CL10B472JB8NNNC SAMSUNG, CL10B472JB8NNNC Datasheet - Page 25

• Manufacturer Part Number: CL10B472JB8NNNC
• Manufacturer: SAMSUNG
• Series: CLr

Specifications of CL10B472JB8NNNC

• Size: 0603
• Dielectric: X7R
• Tolerance: +/- 5%
• Voltage: 50V
• Thickness: 0.80
• Electrode/termination/platin: Ni/Cu/Sn 100%
• Products: Normal

NO
14
15
Multilayer Ceramic Capacitor - General
RESISTANCE
MOISTURE
HUMIDITY
(STEADY
STATE)
ITEM
CAPACITANCE
CAPACITANCE
APPEARANCE
APPEARANCE
RESISTANCE
RESISTANCE
INSULATION
INSULATION
CLASS Ⅰ
CLASS Ⅱ
CLASS Ⅰ
CLASS Ⅱ
Tan δ
Tan δ
Q
Q
NO MECHANICAL DAMAGE SHALL OCCUR
30 ㎊ AND OVER : Q ≥ 350
10 ~30 ㎊
LESS THAN 10pF : Q ≥ 200 + 10 × C
MINIMUM INSULATION RESISTANCE:
1,000 ㏁ OR 50 ㏁∙㎌ PRODUCT WHICHEVER IS
SMALLER
NO MECHANICAL DAMAGE SHALL OCCUR
CLASS
30 ㎊ AND OVER : Q ≥ 200
30 ㎊ AND BELOW : Q ≥ 100 + 10/3 × C
MINIMUM INSULATION RESISTANCE:
500 ㏁ OR 25 ㏁∙㎌ PRODUCT,
WHICHEVER IS SMALLER.
CHARACTERISTIC
CHAR.
CHARACTERISTIC
CLASS
CHAR.
A,B
A,B
F
F
Ⅱ
Ⅱ
CLASS Ⅰ
CLASS Ⅰ
OVER
0.075
MAX
AND
OVER
0.05
25V
0.075
AND
MAX
MAX
0.05
25V
A,B
A,B
: Q ≥ 275 + 2.5 × C
F
F
(C 〈 1.0 ㎌ )
0.05 MAX
(C ≥ 1.0 ㎌ )
(C 〈 1.0 ㎌ )
0.125MAX
(C ≥ 1.0 ㎌ )
PERFORMANCE
0.1MAX
0.1MAX
0.125
MAX
0.05
16V
MAX
16V
WITHIN ± 5% OR
± 0.5 ㎊ WHICHEVER
IS LARGER
WITHIN ± 12.5%
WITHIN ± 30%
CAPACITANCE CHANGE
WITHIN ± 7.5% OR
± 0.75 ㎊ WHICHEVER
IS LARGER
WITHIN ± 12.5%
WITHIN ± 30%
WITHIN +30~ － 40%
1005 C>0.47 μ F
1608 C>1.0 μ F
2012 C>4.7 μ F
3216 C>10.0 μ F
3225 C>22.0 μ F
4532 C>47.0 μ F
CAPACITANCE CHANGE
MAX
MAX
0.05
0.15
10V
MAX
MAX
0.05
0.15
10V
0.075
0.195
6.3V
MAX
MAX
0.075
0.195
6.3V
MAX
MAX
MAX
MAX
0.25
MAX
MAX
0.1
0.25
4V
0.1
4V
TEMPERATURE
RELATIVE HUMIDITY:90~95 %RH
TEST TIME
MEASURE AT ROOM TEMPERATURE
AFTER COOLING FOR
CLASS Ⅰ : 24 ± 2 Hr.
CLASS Ⅱ : 48 ± 4 Hr.
APPLIED VOLTAGE :
TEMPERATURE : 40±2 ℃
RELATIVE HUMIDITY:90~95%RH
TEST TIME : 500 +12/-0 Hr.
CURRENT APPLIED : 50㎃ MAX.
<INITIAL MEASUREMENT>
CLASS Ⅱ SHOULD BE MEASURED
INITIAL VALUE AFTER BE HEAT-TREATED
FOR 1 HR IN 150℃+0/-10℃ AND BE LEFT
FOR 48±4HR AT ROOM TEMPERATURE.
<LATTER MEASUREMENT>
CLASSⅠ SHOULD BE MEASURED AFTER
LEFT FOR 24±2 HRS IN ROOM
TEMPERATURE AND HUMIDITY.
CLASS Ⅱ SHOULD BE MEASURED
LATTER VALUE AFTER BE
HEAT-TREATED FOR 1 HR IN 150℃+0/-10
℃ AND BE LEFT FOR 48±4HR AT ROOM
TEMPERATURE.
CLASS Ⅱ
6.3V
Tan δ
(A,B)
6.3V Tanδ
CLASSⅡ
(A,B)
RATED VOLTAGE
TEST CONDITION
1005 C ≥ 0.22 ㎌
1608 C ≥ 2.2 ㎌
2012 C ≥ 4.7 ㎌
3216 C ≥ 10.0 ㎌
3225 C ≥ 22.0 ㎌
4532 C ≥ 47.0 ㎌
5750 C ≥ 100.0 ㎌
0.125 MAX *Condition
: 500 +12/-0 Hr.
1005 C ≥0.22㎌
1608 C ≥2.2㎌
2012 C ≥4.7㎌
3216 C ≥10.0㎌
3225 C ≥22.0㎌
4532 C ≥47.0㎌
5750 C ≥100.0㎌
0.125 MAX *Condition
: 40 ± 2 ℃
- 24 -