Important Do’s and Don’ts
Discharging
Assembly And Design Considerations
Material for Terminals in Products Using the Batteries
Discharge Temperatures
• Discharge batteries within an ambient temperature range of: Nickel Cadmium -4°F to 149°F (-20°C to 65°C ),
• Discharge capacity will drop when the battery is discharged outside the ambient temperature range
Over-Discharging
• Over-discharging damages the batteries performance. Full discharge has been reached when the the voltage drops
Storage Temperature and Humidity (short-term)
• Store in a dry location with low humidity (Max.85%), within a temperature range of -4°F to 113°F (-20°C to 45°C)
Long-term Storage
• Store within temperature ranges between 50°F to 86°F (10°C to 30°C).
• When charging for the first time after long-term storage, deactivation of the batteries’ chemicals may have led to
Cycle Life
• Significantly reduced discharge time, in spite of proper charging, means that the life of the battery has been
Service Life in Standby Operation
• Normally, a battery will last 3 to 5 years if used under proper conditions. However, failure to satisfy conditions
Connecting Batteries to Products
• Never solder a lead wire or other connecting materials directly to the battery. Doing so will damage the battery’s
• To connect a battery spot-weld a tab made of nickel or nickel-plated steel to the battery’s terminal strip, then solder
• Use caution when disconnecting batteries from the equipment.
• Small amounts of alkaline electrolyte can leak out from the battery seal during a period of extended use or when
Nickel-Metal Hydride 14°F to 122°F (-10°C to 50°C)
to 0.9V to 1.0V, see the individual specification sheets for the applicable details. When the battery has been fully
discharged It should be disconnected from the equipment circuit.
decreased battery capacity. Restore such batteries to original performance through repeating several cycles of
charging and discharging.
exceeded. Also, at the end of service life, an unusual increase in internal resistance, or an internal short-circuit
failure may occur.
concerning charging, discharging, temperature and other factors during actual use can lead to shortened battery
life.
internal safety vent, separator, and other materials.
a lead wire to the tab.
the safety vent is activated during improper use, use a highly alkaline-resistant material for a product’s contact
terminals to avoid problems due to corrosion.