12065E184MAT2A AVX Corporation, 12065E184MAT2A Datasheet - Page 7

• Manufacturer Part Number: 12065E184MAT2A
• Description: Multilayer Ceramic Capacitors (MLCC) - SMD/SMT 1206 0.18uF 50volts Z5U 20%
• Manufacturer: AVX Corporation
• Series: 1206r

Specifications of 12065E184MAT2A

• Capacitance: 0.18 uF
• Tolerance: 20 %
• Voltage Rating: 50 Volts
• Operating Temperature Range: + 10 C to + 85 C
• Temperature Coefficient / Code: Z5U
• Package / Case: 1206 (3216 metric)
• Product: General Type MLCCs
• Dimensions: 1.6 mm (0.063 in) W x 3.2 mm (0.126 in) L
• Dissipation Factor Df: 4
• Termination Style: SMD/SMT
• Lead Free Status / Rohs Status: Details

General Specifications
Environmental
22
THERMAL SHOCK
Specification
Measuring Conditions
IMMERSION
Specification
Measuring Conditions
Step
Step
Appearance
No visual defects
Capacitance Variation
Q, Tan Delta
To meet initial requirement
Insulation Resistance
C0G (NP0), X7R: To meet initial requirement
Z5U, Y5V: ≥ Initial Value x 0.1
Dielectric Strength
No problem observed
Repeat for 5 cycles and measure after 48 hours ± 4 hours
(24 hours for C0G (NP0)) at room temperature.
Appearance
No visual defects
Capacitance Variation
Q, Tan Delta
To meet initial requirement
Insulation Resistance
Dielectric Strength
No problem observed
Repeat cycle 2 times and wash with water and dry.
Store at room temperature for 48 ± 4 hours (24 hours for
C0G (NP0)) and measure.
1
2
3
4
1
2
C0G (NP0): ± 2.5% or ± .25pF, whichever is greater
C0G (NP0): ± 2.5% or ± .25pF, whichever is greater
C0G (NP0), X7R: To meet initial requirement
C0G (NP0), X7R: -55° ± 2°
C0G (NP0), X7R: +125° ± 2°
X7R: ≤ ± 7.5%
Z5U: ≤ ± 20%
X7R: ≤ ± 7.5%
Z5U: ≤ ± 20%
Z5U, Y5V: ≥ Initial Value x 0.1
Y5V: ≤ ± 20%
Y5V: ≤ ± 20%
Room Temperature
Room Temperature
Temperature °C
Temperature °C
NaCl solution
Z5U, Y5V: +85° ± 2°
Pure Water
+65 +5/-0
0 ± 3
Z5U: +10° ± 2°
Y5V: -30° ± 2°
Time (minutes)
Time (minutes)
30 ± 3
30 ± 3
15 ± 2
15 ± 2
# 3
# 3
Specification
Measuring Conditions
Repeat 20 cycles (1-7) and store for 48 hours (24 hours
for C0G (NP0)) at room temperature before measuring.
Steps 7a & 7b are done on any 5 out of first 9 cycles.
MOISTURE RESISTANCE
Step
Appearance
No visual defects
Capacitance Variation
Q, Tan Delta
Insulation Resistance
≥ Initial Value x 0.3
1
2
3
4
5
6
7
7a
7b
C0G (NP0): ± 5% or ± .5pF, whichever is greater
C0G (NP0):≥ 30pF........................Q ≥ 350
X7R: ≤ ± 10%
Z5U: ≤ ± 30%
X7R: Initial requirement + .5%
Z5U: Initial requirement + 1%
Y5V: ≤ ± 30%
Y5V: Initial requirement + 2%
Temp. °C
+25->+65
+65->+25
+25->+65
+65->+25
< 10pF ........................Q ≥ 200+10C
≥ 10pF, < 30pF ...........Q ≥ 275+5C/2
+65
+65
+25
+25
-10
Humidity % Time (hrs)
uncontrolled
90-98
90-98
80-98
90-98
90-98
80-98
90-98
90-98
2.5
3.0
2.5
2.5
3.0
2.5
2.0
–
–