C125R500P Component General, C125R500P Datasheet
C125R500P
Related parts for C125R500P
C125R500P Summary of contents
Page 1
... C62R187P 10 W 0.060" - 0.066" C62R375P 10 W 0.060" - 0.066" C98R062 1/10 W 0.095" - 0.105" C125R406 1/2 W 0.123" - 0.129" C125R500 1/2 W 0.123" - 0.129" C125R500P 20 W 0.123" - 0.129" C250R500P 25 W 0.247" - 0.255" C250R750P 30 W 0.247" - 0.255" C375R750P 60 W 0.370" - 0.380" C125R500S 1/2 W 0.124" - 0.128" Component General Inc. ...
Page 2
P/N:C40R115 www.DataSheet4U.com Mechanical Specifications Substrate Material: Alumina Ceramic. Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. Temperature Coefficient : Standard Temperature Coefficient is - ...
Page 3
P/N:C60R120P www.DataSheet4U.com Mechanical Specifications Substrate Material: Beryllium Oxide Ceramic. (Note: Letter "P" denotes Beryllium Oxide.) Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. Temperature ...
Page 4
P/N:C62R187 www.DataSheet4U.com Mechanical Specifications Substrate Material: Alumina Ceramic. Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. Temperature Coefficient : Standard Temperature Coefficient is - ...
Page 5
P/N:C62R187P www.DataSheet4U.com Mechanical Specifications Substrate Material: Beryllium Oxide Ceramic. (Note: Letter "P" denotes Beryllium Oxide.) Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. Temperature ...
Page 6
P/N:C62R375P www.DataSheet4U.com Mechanical Specifications Substrate Material: Beryllium Oxide Ceramic. (Note: Letter "P" denotes Beryllium Oxide. ) Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. ...
Page 7
P/N:C98R062 www.DataSheet4U.com Mechanical Specifications Substrate Material: Alumina Ceramic. Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. Temperature Coefficient : Standard Temperature Coefficient is - ...
Page 8
P/N:C125R406 www.DataSheet4U.com Mechanical Specifications Substrate Material: Alumina Ceramic. Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. Temperature Coefficient : Standard Temperature Coefficient is - ...
Page 9
P/N:C125R500 www.DataSheet4U.com Mechanical Specifications Substrate Material: Alumina Ceramic. Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. Temperature Coefficient : Standard Temperature Coefficient is - ...
Page 10
... P/N:C125R500P www.DataSheet4U.com Mechanical Specifications Substrate Material: Beryllium Oxide Ceramic. (Note: Letter "P" denotes Beryllium Oxide.) Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. Temperature Coefficient : Standard Temperature Coefficient is - 200 to -300 PPM/° ...
Page 11
P/N:C250R500P www.DataSheet4U.com Mechanical Specifications Substrate Material: Beryllium Oxide Ceramic. (Note: Letter "P" denotes Beryllium Oxide.) Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. Temperature ...
Page 12
P/N:C250R750P www.DataSheet4U.com Mechanical Specifications Substrate Material: Beryllium Oxide Ceramic. (Note: Letter "P" denotes Beryllium Oxide.) Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. Temperature ...
Page 13
P/N:C375R750P www.DataSheet4U.com Mechanical Specifications Substrate Material: Beryllium Oxide Ceramic. (Note: Letter "P" denotes Beryllium Oxide.) Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. Temperature ...
Page 14
P/N:C125R500S www.DataSheet4U.com Mechanical Specifications Substrate Material: Alumina Ceramic. Terminals: Terminal areas are nickel / tin plated wich reduces oxidation thus providing a more solderable terminal. Temperature Range : -55° 200°C. Temperature Coefficient : Standard Temperature Coefficient is - ...