CM05Y5V104Z16AH AVX, CM05Y5V104Z16AH Datasheet - Page 10

• Manufacturer Part Number: CM05Y5V104Z16AH
• Description: CAPACITOR, 0402, 100NF, 16V; Application: Standard; Capacitance: 100000pF; Tolerance, Capacitance: +80%, -20%; Series...
• Manufacturer: AVX

Test conditions and Specification for Temperature Compensation type(C to U • SL characteristics)
1
2
3
4
Capacitance Value
Q
Insulation resistance (IR)
Dielectric Resistance
Appearance
Termination strength
Bending strength
Vibration
test
Soldering
heat
resistance
Solderability
Temperature
cycle
Humidity
test
High-
temperature
with
loading
For the CF series, use 1.5 times when the rated voltage is 250V; use/1.2 times when
the rated voltage exceeds 630V.
Except CT series
Different specification for Nickel Barrier termination DN/DR series. (Alumina Substrate)
Apply 500V for 1minite in case the rated voltage is 1000V or higher.
( 3)
( 5)
Test Items
Appearance
Q
Appearance
Q
IR
Withstand voltage
Appearance
Q
IR
Withstand voltage
Appearance
Q
IR
Appearance
Q
IR
C
C
C
C
C
( 6)
( 6)
( 6)
( 6)
( 2)
( 2)
( 6)
( 6)
( 6)
( 6)
Within tolerance
C 30pF: Q 1000
C<30pF: Q 400 20C
10,000M or 500M • F min, whichever is less
No problem observed
No problem observed
No problem observed
No mechanical damage at 1mm bent
No significant change is detected.
Within tolerance
C 30pF: Q 1000
C<30pF: Q 400 20C
No significant change is detected.
C 30pF: Q 1000
C<30pF: Q 400 20C
10,000M or 500M • F min, whichever is smaller
Resists without problem
Ni/Br termination: 90% min
No significant change is detected.
C 30pF: Q 1000
C<30pF: Q 400 20C
10,000M or 500M • F min, whichever is samller
Resists without problem
No significant change is detected.
C 30pF: Q 200
C<30pF: Q 100 10C/3
500M or 25M • F min, whichever is smaller
No significant change is detected.
C 30pF: Q 350
10pF C<30pF: Q 275 5C/2
C<10pF: Q 200 10C
1,000M or 50M • F min, whichever is smaller
2.5% or 0.25pF max, whichever is larger.
2.5% or 0.25pF max, whichever is larger.
7.5% or 0.75pF max, whichever is larger.
3% or 0.3pF max, whichever is larger.
Specification (C: nominal capacitance)
5
6
7
Multilayer Ceramic Chip Capacitors
Except CF series.
The charge and discharge current of the capacitor must not exceed 50mA.
2N at 0201 Size
Test Conditions and Standards
Measured after the rated voltage is applied for one
minute at normal room temperature and humidity. ( 4)
( 1) Apply 3 times of the rated voltage for 1 to 5 seconds.
Microscope(10 magnification)
Apply a sideward force of 500g(5N) ( 7) to a PCB-mounted
sample.
Glass epoxy PCB (t=1.6mm); fulcrum
Spacing: 90mm; for 10 seconds.
Vibration frequency: 10 to 55(Hz)
Amplitude: 1.5mm
Sweeping condition: 10 55 10Hz/min
In X, Y and Z directions:
2 hours each Total 6 hours
Soak the sample in 260 C 5 C
solder for 10 0.5seconds
and place in a room at normal temperature
and humidity; measure after 24 2hours.
(Preheating Conditions)
Soaking Condition
(Cycle)
Normal room temperature (3min)
Lowest operation temperature (30min)
Normal room temperature (3min)
Highest operation temperature (30min)
After five cycles
24 2hours.
Measure the test sample after storing it
24 2hours at a temperature of 40 C 2 C
and a relative humidity of 90-95% Rh.
for 500 24/ 0hours.
After applying
at a temperature of 125 3 C for
1000 48/ 0hours, measure the sample
after storing 24 2hours.
Sn63 Solder
Sn-3Ag-0.5Cu
Order
C>1000pF
C 1000pF
1
2
Test Conditions
Temperature
150 to 200 C
( 1)
80 to 100 C
( 3)
twice of the rated voltage
1MHz 10%
235 5 C
245 5 C
1kHz 10%
, measure after
2 0.5sec.
3 0.5sec.
2minutes
2minutes
0.5 to
5Vrms
Time