SMK432B7473KM-T Taiyo Yuden, SMK432B7473KM-T Datasheet - Page 13
![CAP CER 47000PF 630V X7R 1812](/photos/10/53/105304/hmk_jmk_lmk_qmk_smk_tmk_umk_series_1812_sml.jpg)
SMK432B7473KM-T
Manufacturer Part Number
SMK432B7473KM-T
Description
CAP CER 47000PF 630V X7R 1812
Manufacturer
Taiyo Yuden
Series
SMKr
Specifications of SMK432B7473KM-T
Capacitance
0.047µF
Voltage - Rated
630V
Tolerance
±10%
Temperature Coefficient
X7R
Mounting Type
Surface Mount, MLCC
Operating Temperature
-55°C ~ 125°C
Features
High Voltage
Applications
General Purpose
Package / Case
1812 (4532 Metric)
Size / Dimension
0.177" L x 0.126" W (4.50mm x 3.20mm)
Thickness
2.50mm
Capacitor Application
High Voltage
Dielectric Characteristic
X7R
Capacitance Tolerance
± 10%
Voltage Rating
630VDC
Capacitor Case Style
1812
No. Of Pins
2
Rohs Compliant
Yes
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Ratings
-
Lead Spacing
-
Other names
587-1398-2
CG SMK432 BJ473KM-T
CG SMK432 B7473KM-T
SMK432BJ473KM-T
CG SMK432 BJ473KM-T
CG SMK432 B7473KM-T
SMK432BJ473KM-T
Available stocks
Company
Part Number
Manufacturer
Quantity
Price
Company:
Part Number:
SMK432B7473KM-T
Manufacturer:
TAYO YUDEN
Quantity:
360 000
MEDIUMーHIGH VOLTAGE MULTILAYER CERAMIC CAPACITOR
△
1.Operating Temperature Range
2.Storage Temperature Range
3.Rated Voltage
4.Withstanding Voltage
5.Insulation Resistance
6.Capacitance (Tolerance)
7.Tangent of Loss Angel
8.Temperature Characteristic
9.Resistance to Flexure of
10.Adhesion of Electrode
11.Solderability
12.Resistance to Soldering
13.Thermal shock
!
RELIABILITY DATA
Between terminals
Substrate
of Capacitance
当社カタログをご使用の際には 「当社製品に関するお断り」 を必ずお読みください。
Item
X7R, X7S:ー55 to +125℃ B: ー25 to +85℃
X7R, X7S :ー55 to +125℃ B: ー25 to +85℃
100VDC, 250VDC, 630VDC
No breakdown or damage
100MΩμF or 10GΩ, whichever is smaller.
±20%、±10%
3.5%max (100V) .
2.5%max (250V, 630V) .
B: ±10% (ー25 to +85℃)
X7R: ±15% (ー55 to +125℃)
X7S: ±22%(−55 to +125℃)
Appearance:No abnormality Capacitance change:Within±10%
No separation or indication of separation of electrode
At least 75% of terminal electrode is covered by solder
Appearance:No abnormality
Capacitance change:Within±15% (100V) , ±10% (250V, 630V)
tanδ: Initial value
Insulation resistance:Intial value
Withstanding voltage (between terminals) : No abnormality
Appearance:No abnormality
Capacitance change:Within±15% (100V) , ±7.5% (250V, 630V)
tanδ: Initial value
Insulation resistance:Initial value
Specified Value
9
△
!
Please read the "Notice for TAIYO YUDEN products" before using this catalog.
Applied voltage:Rated voltage×2.5 (100V) Rated voltage×2 (250V) Rated voltage×1.2 (630V)
Duration:1∼5sec.
Chage/dischage current:50mAmax.
Applied voltage:Rated voltage (100V, 250V) 500V (630V)
Duration:60±5sec.
Chage/dischage current:50mAmax.
Measuring frequency:1kHz±10%
Measuring voltage:1±0.2Vrms
Bias application:None
Measuring frequency:1kHz±10%
Measuring voltage:1±0.2Vrms
Bias application:None
According to JIS 5102 clause7.12.
Charge of maximum capacitance deviation in step 1 to 5
Temperature at step 1:+25℃
Temperature at step 2:minimum operating temperature
Temperature at step 3:+25℃(Reference temperature)
Temperature at step 4:maximum operating temperature
Temperature at step 5:+25℃
Reference temperature Characteristic B shall be +20℃
Warp:1mm
Testing boade:glass epoxyーresin substrate
Thickness:1.6mm
The measurement shall be made with board in the bent
position
Applied force:5N
Duration:30±5sec.
Solder temperature:230±5℃
Duration:4±1sec.
Preconditioning:Thermal treatment ( at 150℃ for 1hr)
Solder temperature:270±5℃
Duration:3±0.5sec.
Preheating conditions: 80 to 100℃, 2 to 5 min.
Recovery:Rcovery for the following reriod under the
standerd condition after the test.
24±2hrs
Preconditioning:Thermal treatment ( at 150℃ for 1hr)
Conditions for 1 cycle
Step 1:Minimum operating temperature +0/−3℃ 30±3min.
Step 2:Room temperature
Step 3:Maximum operating temperature +0/−3℃ 30±3min.
Step4:Room temperature
Number of cycles:5 times
Recovery after the test:24±2hrs
Test Methods and Remarks
150 to 200℃, 2 to 5min.
R-230
2 to 3min.
2 to 3min.
1/2
85