Surface-Mount Ceramic Multilayer Capacitors
Table 14 Test condition, procedure and requirements (continued)
TEST
TEST METHOD
Resistance to
4.9
soldering heat
Solderability
4.10
Rapid change
IEC 60384-22 4.11
of
temperature
Damp heat
4.13
steady state
Endurance
4.14
June 1, 2006 V.11
High-Capacitance
PROCEDURE
Precondition: 150 +0/–10 °C for 1 hour, then keep for 24
±1 hours at room temperature
Preheating: for size ≤ 1206: 120 to 150 °C for 1 minute
Preheating: for size >1206: 100 to 120 °C for 1 minute
and 170 to 200 °C for 1 minute
Solder bath temperature: 260 ±5 °C
Dipping time: 10 ±0.5 seconds
Recovery time: 24 ±2 hours.
Unmounted chips completely immersed in a solder bath at
235 ±5 °C
Dipping time: size ≤ 1206 for 2 ±0.5 seconds; size > 1206
for 4 ±0.5 seconds
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for 24 ±1 hours at
room temperature
5 cycles with following detail:
30 minutes at lower category temperature;
30 minutes at upper category temperature
Recovery time 24 ±2 hours.
Initial measurements; after 150 +0/-10 °C for 1 hour, then
keep for 24 ±1 hours at room temperature
Duration and conditions: 500 ±12 hours at 40 ±2 °C;
90 to 95% RH
Final measurement: perform a heat treatment at 150 +0/–
10 °C for 1 hour, final measurements shall be carried out
24 ±1 hours after recovery at room temperature without
load.
Preconditioning;
Initial measurements; after 150 +0/-10 °C for 1 hour, then
keep for 24 ±1 hours at room temperature
Duration and conditions: 1,000 ±12 hours at upper
category temperature with 1.5 × U
voltage applied
r
Final measurement: perform a heat treatment at 150 +0/–
10 °C for 1 hour, final measurements shall be carried out
24 ±1 hours after recovery at room temperature without
load.
14
Product specification
16
/
6.3 V to 25 V
X5R
X7R
REQUIREMENTS
The termination shall be well
tinned
X5R/X7R: lΔC/Cl: ≤ 10%
Y5V: lΔC/Cl: ≤ 20%
D.F.: within initial specified value
R
: within initial specified value
ins
The termination shall be well
tinned.
No visual damage
X5R/X7R: ≤ 15%
Y5V: ≤ 20%
D.F.: within initial specified value
R
: within initial specified value
ins
X5R/X7R: lΔC/Cl: ±20%
Y5V: lΔC/Cl: ±30%
D.F.: 2 × initial value max.
R
: 1,000 MΩ or R
× C
≥ 50
ins
ins
r
seconds, whichever is less
X5R/X7R: lΔC/Cl: ±20%
Y5V: lΔC/Cl: ±30%
D.F.: 2 × initial value max.
R
: 1,000 MΩ or R
× C
≥ 50
ins
ins
r
seconds, whichever is less
www.yageo.com