TEST
Rapid change
of
temperature
Damp heat
Surface-Mount Ceramic Multilayer Capacitors
TEST METHOD
IEC 60384-
21/22
4.11
4.13
PROCEDURE
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for
24 ±1 hours at room temperature
5 cycles with following detail:
30 minutes at lower category temperature
30 minutes at upper category temperature
Recovery time 24 ±2 hours
1.
2.
3.
4.
5.
P.S. If the capacitance value is less than the
minimum value permitted, then after the
other measurements have been made the
capacitor shall be precondition according to
“IEC 60384 4.1” and then the requirement
shall be met.
Preconditioning, class 2 only:
150 +0/-10 °C /1 hour, then keep for
24 ±1 hour at room temp
Initial measure:
Spec: refer initial spec C, D, IR
Damp heat test:
500 ±12 hours at 40 ±2 °C;
90 to 95% R.H.
Recovery:
Class 1: 6 to 24 hours
Class 2: 24 ±2 hours
Final measure: C, D, IR
Mid-voltage
REQUIREMENTS
No visual damage
∆C/C
Class 1:
NP0: within ±1% or 1 pF, whichever is greater
Class2:
X7R: ±15%
D.F. meet initial specified value
R
No visual damage after recovery
∆C/C
Class 1:
NP0: within ±2% or 1 pF, whichever is greater
Class2:
X7R: ±15%
D.F.
Class 1:
NP0: ≤ 2 x specified value
Class2:
X7R: ≥ 25 V: ≤ 5%
R
Class 1:
NP0: ≥ 2,500 MΩ or R
Class2:
X7R: ≥ 500 MΩ or R
ins
ins
meet initial specified value
NP0
/
X7R
ins
ins
x C
100 V to 630 V
x C
r
≥ 25s whichever is less
r
≥ 25s whichever is less