RS341 Stackpole Electronics, RS341 Datasheet - Page 4

• Manufacturer Part Number: RS341
• Description: RES / METAL OXIDE
• Manufacturer: Stackpole Electronics

Page A-2
Thick Film Chip Resistors
SEI Type RMC
Rev. 07/98
Note 1. Maximum solder flow process “Normal” 275°C, 30 seconds or the “SM10” process @ 310°C for 10 seconds.
Moisture Resistance, Thermal Shock
Low Temperature Exposure
Load Life
Load Life in Moisture
Vibration
Resistance to Soldering Heat
Solderability
Heat
Resistance
Terminal
Strength
Dielectric Withstanding Voltage
Short Time Overload
Insulation Resistance
Voltage Coefficient
ENVIRONMENTAL
SEI Electronics Inc.
ORDERING INFORMATION
Type
Resistance value in three-digit designation system is marked
on the glasscoat. Illustrated is a resistor of 15K . Four-digit
resistance designation system is applied to RMC 1/8 and E-96
Series. For example, 1502 designated 15K . (The last digit
specifies the number of zeros.)
Adhesion Curing
Board Bending
Toll Free: (888) SEI-SEI-SEI
Dry Heat
Wattage
Pull
RMC 1/16 1K 1%
P.O. Box 58789
Resistance
(1% +0.05 ), No Mechanical Damage
(1% +0.05 ), No Mechanical Damage
(1% +0.05 ), No Mechanical Damage
(1% +0.05 ), No Mechanical Damage
(1% +0.05 ), No Mechanical Damage
Marking
Specification Requirement
(3% +0.1 ), No Mechanical Damage
(3% +0.1 ), No Mechanical Damage
<1meg (3% +0.1 ), 1meg 5%
<1meg (3% +0.1 ), 1meg 5%
(1% +0.05 ), No evidence of arc
+0/-100ppm/V (above 1K )
No insulation breakdown
PERFORMANCE CHARACTERISTICS
Substrate
Resistive Film
Coating
Terminations
Feature
1,000 meg minimum
min. 95% coverage
Tolerance
(1% +0.05 )
www.seielect.com
Raleigh, NC 27658-8789
MATERIALS
MARKING
Alumina Porcelain
Ruthenium-Oxide Film
Boro-Silicated Acid Lead Glass
90/10 Tin-Lead (Electrical Plated) over
Nickel (Electrical Plated) over
AG-PD (Silver-Palladium[Glaze Printed])
Material
1. RMC 1/16 is Dual Rated at 1/10W.
2. RMC 1/10 is Dual Rated at 1/8W.
3. RMC 1/8 is Dual Rated at 1/4W.
4. RMC 1/4 is Dual Rated at 3/4W.
5. Zero ohm (0.05 max.) jumper available in all sizes.
email: [e-mail]
40°C, 95% R.H., 1.5hr on/0.5hr off, 1,000 hrs
70°C, rated voltage, 1.5hr on/0.5hr off, 1000 hrs
Rated voltage & 1/10 times rated voltage
Tested per EIA J-RC-2690A
2
Telephone: [phone]
10-55 Hz, 3 direction, each 2 hours
1
230°C, 3 seconds, flux applied
/
2
1/45mm bend, 10 seconds
-55°C to +125°C, 5 cycles
times rated voltage, 5 seconds
500G load, 30 seconds
-125°C, 1,000 hours
+150°C, 10 minutes
-55°C, 1,000 hours
270°C, 10 seconds
500V, 1 minute
500V, 1 minute
* For 1%, a 3-digit alpha-numeric
marking system is used. Contact
factory for details.
5% 3-digit
0603*
0805
1206
1210
2010
2512
NOTES
ISO 9002 Registered
Purity 96% min.
20 Microns Thick
20 Microns Thick
Remarks (Reference Only)
3 Microns Thick
3 Microns Thick
8 Microns Thick
1
FAX: [phone]
1% 4-digit
0805
1206
1210
2010
2512
Within -90ppm/V
More than 97%
Above 10
Within 0.2%
Within 0.5%
Within 0.1%
Within 0.3%
Within 0.5%
Within 0.2%
Within 0.2%
Within 0.4%
Above 900V
See graph
See graph
See graph
Typical
6
meg