C4520C0G3F220K TDK Corporation, C4520C0G3F220K Datasheet - Page 7

• Manufacturer Part Number: C4520C0G3F220K
• Description: CAP CER 22PF 3000V C0G 10% 1808
• Manufacturer: TDK Corporation
• Series: Cr

Specifications of C4520C0G3F220K

• Capacitance: 22pF
• Tolerance: ±10%
• Package / Case: 1808 (4520 Metric)
• Voltage - Rated: 3000V (3kV)
• Temperature Coefficient: C0G, NP0
• Mounting Type: Surface Mount, MLCC
• Operating Temperature: -55°C ~ 125°C
• Features: High Voltage
• Applications: General Purpose
• Size / Dimension: 0.177" L x 0.079" W (4.50mm x 2.00mm)
• Thickness: 1.10mm
• Voltage Rating: 3 KVolts
• Operating Temperature Range: - 55 C to + 125 C
• Temperature Coefficient / Code: C0G (NP0)
• Product: High Voltage MLCCs
• Dimensions: 2 mm W x 4.5 mm L
• Termination Style: SMD/SMT
• Capacitor Application: High Voltage
• Dielectric Characteristic: C0G / NP0
• Capacitance Tolerance: ± 10%
• Capacitor Case Style: 1808
• No. Of Pins: 2
• Rohs Compliant: Yes
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant
• Ratings: -
• Lead Spacing: -
• Lead Free Status / Rohs Status: Lead free / RoHS Compliant
• Other names: 445-2367-2; C4520C0G3F220KT; C4520COG3F220K

• All specifications are subject to change without notice. Please read the precautions before using the product.
No.
10
11
12
General
Specifications
Item
Solderability
Vibration
External
appearance
Capacitance
Q (Class 1)
D.F. (Class 2)
Temperature cycle
External
appearance
Capacitance
Q (Class 1)
D.F. (Class 2)
Insulation
Resistance
Voltage
Proof
Performance
New solder to cover over 75% of
termination.
25% may have pin holes or rough spots
but not concentrated in one spot.
Ceramic surface of “A sections” shall
not be exposed due to melting or
shifting of termination material.
No mechanical damage.
Meet the initial spec.
No mechanical damage.
Meet the initial spec.
Meet the initial spec.
No insulation breakdown or other
damage.
Characteristics
Class 1
Class 2
Rated Capacitance
30pF and over
Under 30pF
Characteristics
Class 1
Class 2
Rated Capacitance
30pF and over
Under 30pF
C0G
X7R
C0G
X7R
C : Rated capacitance (pF)
C : Rated capacitance (pF)
A section
Change from the
value before test
±2.5 %
± 7.5 %
Change from the
value before test
±2.5 %
± 7.5 %
C Series — High Voltage Application
Q
1,000 min.
400+20×C min.
Q
1,000 min.
400+20×C min.
Test or Inspection Method
Completely soak both terminations in solder at
235±5ºC for 2±0.5s.
Solder: H63A (JIS Z 3282)
Flux: Isopropyl alcohol (JIS K 8839)
Completely soak both terminations in solder at
260±5ºC for 5±1s.
Preheating condition
Flux: Isopropyl alcohol (JIS K 8839)
Solder: H63A (JIS Z 3282)
Leave the capacitor in ambient conditions for 6 to 24h
(Class 1) or 24±2h (Class 2) before measurement.
Reflow solder the capacitor on P.C. board (shown
in Appendix 1) before testing.
Expose the capacitor in the conditions step1
through step 4 and repeat 5 times consecutively.
Leave the capacitor in ambient conditions for 6 to
24h (Class 1) or 24±2h (Class 2) before
measurement.
US Catalog // C Series — High Voltage Application // Version A11
Step
1
2
3
4
Temp.: 150±10ºC
Time: 1 to 2min.
Rosin (JIS K 5902) 25% solid solution.
Rosin (JIS K 5902) 25% solid solution.
Temperature (ºC)
Min. operating temp. ±3
Reference Temp.
Max. operating temp. ± 2
Reference Temp.
Time (min.)
30 ± 3
2 — 5
30 ± 2
2 - 5