DP-125 GRAY 1.7 FL OZ 3M, DP-125 GRAY 1.7 FL OZ Datasheet - Page 4
DP-125 GRAY 1.7 FL OZ
Manufacturer Part Number
DP-125 GRAY 1.7 FL OZ
Description
EPOXY 2 PART ADH DUAL CART 1.7FL.OZ
Manufacturer
3M
Series
Scotch Weldr
Datasheet
1.DP-125_GRAY_1.7_FL_OZ.pdf
(7 pages)
Specifications of DP-125 GRAY 1.7 FL OZ
Adhesive Type
Epoxy - 2 Part
Adhesive Applications
Bonding - General Purpose
Color
Gray
Dispensing Method
Dual-Cartridge
Volume
1.7fl.oz. (US)
Pack Quantity
2
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
3M
Epoxy Adhesives
DP125 Translucent and Gray
Typical Adhesive
Performance
Characteristics
(continued)
™
Scotch-Weld
Note: The following technical information and data should be considered representative
Overlap Shear Strength vs Temperature
(Bonds cured 24 hr @ RT + 2 hrs @ 160°F)
Solvent Resistance
Footnotes:
12. Overlap shear (OLS) strengths were measured on 1 in. wide 1/2 in. overlap specimens. These bonds were made
13. T-peel strengths were measured on 1 in. wide bonds at 73°F. The testing jaw separation rate was 20 inches per minute.
14. Solvent resistance was determined using cured (24 hrs RT + 2 hrs 160°F) samples (1/2 in. x 4 in. x 1/8 in. thickness)
180° Peel Strength vs Temperature
(Bonds cured 24 hr @ RT + 2 hrs @ 160°F)
Bonds tested at
-67°F
70°F
120°F
150°F
180°F
Acetone
Isopropyl Alcohol
Freon TF
Freon TMC
1,1,1-Trichlorethane
RMA Flux
Key: A - Unaffected, B - Slight Attack, C - Moderate/Severe Attack
-67°F
70°F
120°F
150°F
180°F
individually using 1 in. x 4 in. pieces of substrate. The thickness of the bond line was 0.005-0.008 in. All strengths were
measured at 70°F except were noted. (Test per ASTM D 1002-72.)
The separation rate of the testing jaws was 0.1 in. per minute for metals, 2 in. per minute for plastics and 20 in. per minute
for rubbers. The thickness of the substrates were: steel, 0.060 in.; other metals, 0.05-0.064 in.; rubber, 0.125 in.; plastics,
0.125 in.
The substrates were 0.020 in. thick. (Tests per ASTM D 1876-61T.)
immersed in the test solvent for 1 hour and 1 month. After the allotted period of time the sample was removed and visually
examined for surface attack as compared to the control.
™
or typical only and should not be used for specification purposes.
14
Scotch-Weld Epoxy Adhesive Scotch-Weld Epoxy Adhesive
Scotch-Weld Epoxy Adhesive Scotch-Weld Epoxy Adhesive
- 4 -
One Hour/One Month
3M™ Scotch-Weld™
DP125 Translucent
DP125 Translucent
DP125 Translucent
Epoxy Adhesive
4000 psi
2500 psi
13
35 piw
10 piw
400 psi
190 psi
150 psi
3 piw
3 piw
2 piw
A/A
A/A
A/A
A/B
A/A
A/A
12
One Hour/One Month
3M™ Scotch-Weld™
Epoxy Adhesive
DP125 Gray
DP125 Gray
DP125 Gray
3400 psi
4300 psi
35 piw
18 piw
700 psi
450 psi
400 psi
3 piw
3 piw
2 piw
A/A
A/A
A/A
A/B
A/A
A/A