DP-110-GRAY-200ML 3M, DP-110-GRAY-200ML Datasheet - Page 4

• Manufacturer Part Number: DP-110-GRAY-200ML
• Description: Adhesive; Epoxy; Gray; Duo-Pak; 200 mL Tube
• Manufacturer: 3M

Specifications of DP-110-GRAY-200ML

• Chemical Component: Butadiene/Epoxy Resin/Hydrogenated Polyphenyls/Hydrogenated Terphenyl/Methacrylate/Styrene Polymer
• Chemical System: Epoxy
• Color: Gray
• Dispensing Method: Syringe
• Primary Type: Adhesive
• Time, Drying: Air Dry for 15 minutes, Force Dry for 10 minutes @ 66 °C +⁄- 23 °C (Aluminum Surface), If 3M™ Scotch-Weld™ Structural Adhesive Primer EC1945 B⁄A is Used, Apply a Thin Coating (0.5 mils) on the Metal Surfaces to be Bonded, Air Dry for 60 minutes, then Cure
• Time, Setting: 15 min. (Aluminum), 60 min. (Steel)
• Weight: 200 ml

Scotch-Weld
Epoxy Adhesives
DP110 Translucent and Gray
Typical Cured
Electrical Properties
Typical Adhesive
Performance
Characteristics
Typical Cured
Thermal Properties
TM
Note: The following technical information and data should be considered representative
The following product performance data was obtained in the 3M laboratory under
the conditions specified. The following data show typical results obtained with
Scotch-Weld epoxy adhesive DP110 Translucent and Gray when applied to
properly prepared substrates and cured for 48 hours at 73°F (23°C) under 2 psi
pressure and tested according to the specifications indicated.
Note: All data developed after a 48 hour cure @ 75°F (24°C) under 2 psi pressure
A. Aluminum Overlap Shear
Note: The following technical information and data should be considered representative
Note: The following technical information and data should be considered representative
Product
Dielectric Strength (volts/mil)
Volume Resistivity (ohms - cm)
Product
Thermal Conductivity
BTU/Hr/Ft
Thermal Coefficient of Expansion
Glass Transition Temp.
Overlap shear shear strength was measured on FPL etched 1 in. wide by 1/2 in.
overlap specimens. The bonds were made from 2 panels of 4 in. x 7 in. x .063 in.,
2024 T3 clad aluminum bonded together and cut into 1 in. wide specimens. The
separation rate of the testing jaws was .1 in./minute. Tests similar to ASTM D-1002.
or typical only and should not be used for specification purposes.
or typical only and should not be used for specification purposes.
or typical only and should not be used for specification purposes.
160°F (71°C)
180°F (82°C)
unless noted otherwise.
-67°F (-55°C)
Test Temp
75°F (24°C)
-58°F (-50°C) - 32°F (0°C)
-58°F (-50°C) - 166°F (110°C)
2
/°F/Ft.
- 2 -
DP110 Translucent
Epoxy Adhesive
Scotch-Weld
2500 psi
2500 psi
270 psi
200 psi
3M™ Scotch-Weld™
.106 @ 113°F (45°C)
DP110 Translucent
DP110 Translucent
Epoxy Adhesive
Epoxy Adhesive
Scotch-Weld
55°F (13°C)
200 x 10
4.5 x 10
80 x 10
520
-6
10
-6
Epoxy Adhesive
Scotch-Weld
3M™ Scotch-Weld™
DP110 Gray
.104 @ 113°F (45°C)
Epoxy Adhesive
Epoxy Adhesive
2700 psi
3500 psi
270 psi
250 psi
Scotch-Weld
DP110 Gray
DP110 Gray
61°F (16°C)
165 x 10
6.9 x 10
73 x 10
470
-6
10
-6