62-2324-2001-8 3M, 62-2324-2001-8 Datasheet - Page 5

• Manufacturer Part Number: 62-2324-2001-8
• Description: TAPE SCOTCH-WELD 4IN X 36YD
• Manufacturer: 3M
• Series: Scotch-Weld™r

Specifications of 62-2324-2001-8

• Tape Type: Film
• Adhesive: Epoxy Thermosetting
• Backing, Carrier: Crepe Paper
• Thickness: 0.0179" (17.9 mils, 0.455mm)
• Thickness - Adhesive: 0.0100" (10.0 mils, 0.254mm)
• Thickness - Backing, Carrier, Liner: 0.0079" (7.9 mils, 0.201mm)
• Width: 4.00" (101.60mm) 1/3'
• Length: 108' (32.9m) 36 yds
• Color: White, Off
• Usage: Bonding
• Temperature Range: 250°F (121°C) - 60 minutes
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant
• Other names: Q5481988

3
Bonding Film
AF111 for Electronics Applications
Adhesion Retention
Values After
Environmental Aging
Solvent Resistance of
Cured Films After 60
Days Immersion at RT
Note: The following technical information and data should be considered representative
* Peel bonds consisted of 10 mil etched aluminum strips bonded to 0.047" FR-4. Panels were
• Hot/cold cycle was 17 hours at 120°F (49°C) and 5 hours at -5°F (-21°C) with one hour at
* OLS (overlap shear) bonds consisted of 3M™ Scotch-Brite™ Scour Pad (green) abraded
• Hot/cold cycle was 17 hours at 120°F (49°C) and 5 hours at -5°F (-21°C) with one hour at
• Samples were cured according to data sheet instructions [60 minutes at 250°F (121°C)]
• After 60 days, samples were removed, dried, and examined for swelling and surface attack.
Aging Parameters
30 days at room temperature (control)
30 days at 160°F (71°C) oven
30 days at 120°F (49°C)/100% RH
30 days immersion in distilled water
Hot/cold cycling
Aging Parameters
30 days at room temperature (control)
30 days at 160°F (71°C) oven
30 days at 120°F (49°C)/100% RH
30 days immersion in distilled water
Hot/cold cycling
Aging Parameters
Isopropyl Alcohol
Methyl Ethyl Ketone
Heptane
3M™ Citrus Base Cleaner
cured 60 minutes + 7 minutes (ramp time) at 250°F (121°C) and peeled at 2"/minute speed.
room temperature between temperature changes.
CRS to CRS, cured 60 minutes + 7 minutes (ramp time) at 250°F (121°C) and tested at
0.2"/minute speed.
room temperature between temperature changes.
and immersed in test solvents.
or typical only and should not be used for specification purposes.
- 5 -
3M™ Bonding Film AF111 Peel*
Bonding Film AF111 OLS*
Bonding Film AF111
No Attack
No Attack
No Attack
No Attack
1200 psii
2300 psi
2600 psi
1600 psi
2400 psi
33 piw
33 piw
32 piw
35 piw
33 piw