GA355QR7GF332KW01L Murata Electronics North America, GA355QR7GF332KW01L Datasheet - Page 118

• Manufacturer Part Number: GA355QR7GF332KW01L
• Description: CAP CER 250VAC 3300PF X7R 2220
• Manufacturer: Murata Electronics North America
• Series: GFr

Specifications of GA355QR7GF332KW01L

• Capacitance: 3300pF
• Voltage - Rated: 250VAC
• Tolerance: ±10%
• Temperature Coefficient: X7R
• Mounting Type: Surface Mount, MLCC
• Operating Temperature: -55°C ~ 125°C
• Features: High Voltage
• Applications: Safety
• Ratings: X1Y2
• Package / Case: 2220 (5750 Metric)
• Size / Dimension: 0.224" L x 0.197" W (5.70mm x 5.00mm)
• Thickness: 1.50mm
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant
• Lead Spacing: -
• Other names: 490-3481-2

!Note
• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our
• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
sales representatives or product engineers before ordering.
!Note
!Note
116
No.
13
14
15
Mounting for testing: The capacitors should be mounted on the substrate as shown below using die bonding and wire bonding when tests No. 11 to 15 are performed.
GMA Series Specifications and Test Methods (1)
GMA Series Specifications and Test Methods (1)
Alumina substrate
Continued from the preceding page.
Humidity
(Steady State)
Humidity
Load
High
Temperature
Load
1. This Specifications and Test Methods is downloaded from the website of Murata Manufacturing co.,ltd. Therefore, it's specifications are subject to change or our products in it may be discontinued without advance notice.
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
0.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
2. This Specifications and Test Methods has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product
0.
Please check with our sales representatives or product engineers before ordering.
specifications before ordering.
Item
Appearance No defects or abnormalities
Capacitance
Change
D.F.
I.R.
Appearance No defects or abnormalities
Capacitance
Change
D.F.
I.R.
Appearance No defects or abnormalities
Capacitance
Change
D.F.
I.R.
R7: Within 12.5%
R7: W.V.: 10V min.; 0.05 max.
More than 1,000M or 50 F
(whichever is smaller)
R7: Within 12.5%
R7: W.V.: 10V min.; 0.05 max.
More than 500M or 25 F
(whichever is smaller)
R7: Within 12.5%
R7: W.V.: 10V min.; 0.05 max.
More than 1,000M or 50 F
(whichever is smaller)
Gold land
Die bond
Capacitor
When no "*" is added in PNs table, please refer to GMA Series Specifications and Test Methods (1).
Specifications
When "*" is added in PNs table, please refer to GMA Series Specifications and Test Methods (2).
Alumina substrate
Gold wire
Set the capacitor for 500 12 hours at 40 2 C, in 90 to 95%
humidity.
Take it out and set it for 24 2 hours at room temperature, then
measure.
Apply the rated voltage for 500 12 hours at 40 2 C, in 90 to
95% humidity and set it for 24 2 hours at room temperature,
then measure. The charge/discharge current is less than 50mA.
A voltage treatment should be given to the capacitor, in which a
DC voltage of 200% the rated voltage is applied for one hour at
the maximum operating temperature; 3 C then it should be set
for 24 2 hours at room temperature and the initial measurement
should be conducted.
Then apply the above mentioned voltage continuously for
1000 12 hours at the same temperature, remove it from the
bath, and set it for 24 2 hours at room temperature, then
measure. The charge/discharge current is less than 50mA.
Gold land
Test Method
C02E.pdf
10.12.20