GRM155R60J225ME15D Murata, GRM155R60J225ME15D Datasheet - Page 218

• Manufacturer Part Number: GRM155R60J225ME15D
• Manufacturer: Murata

Specifications of GRM155R60J225ME15D

• Tolerance (+ Or -): 20%
• Voltage: 6.3VDC
• Temp Coeff (dielectric): X5R
• Operating Temp Range: -55C to 85C
• Mounting Style: Surface Mount
• Construction: SMT Chip
• Case Style: Ceramic Chip
• Failure Rate: Not Required
• Wire Form: Not Required
• Product Length (mm): 1mm
• Product Depth (mm): 0.5mm
• Product Height (mm): 0.5mm
• Product Diameter (mm): Not Requiredmm
• Capacitance: 2.2uF
• Package / Case: 0402
• Lead Free Status / RoHS Status: Compliant

18
!Note
• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our
• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
sales representatives or product engineers before ordering.
!Note
4. Cleaning
5. Resin Coating
1. Capacitance change of capacitor
216
(1) In case of X7R char.
(2) In case of any char. except X7R
Notice
Capacitors have an aging characteristic, whereby
the capacitor continually decreases its
capacitance slightly if the capacitor is left on
for a long time. Moreover, capacitance might change
greatly depending on the surrounding temperature
or an applied voltage. So, it is not likely to be
suitable for use in a time constant circuit.
Please contact us if you need detailed information.
Capacitance might change a little depending on the
surrounding temperature or an applied voltage.
Please contact us if you intend to use this product
in a strict time constant circuit.
Rating
Please confirm there is no problem in the reliability of the
product beforehand when cleaning it with the intended
equipment.
The residue after cleaning it might cause the decrease in
the surface resistance of the chip and the corrosion of the
electrode part, etc. As a result it might cause reliability to
deteriorate. Please confirm beforehand that there is no
problem with the intended equipment in ultrasonic
cleansing.
Please use it after confirming there is no influence on the
product with a intended equipment beforehand when the
resin coating and molding.
A cracked chip might be caused at the cooling/heating
cycle by the amount of resin spreading and/or bias
thickness.
The resin for coating and molding must be selected as
the stress is small when stiffening and the hygroscopic is
low as possible.
Continued from the preceding page.
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
2. Performance check by equipment
Before using a capacitor, check that there is no
problem in the equipment's performance and the
specifications.
Generally speaking, CLASS 2 (X7R char.) ceramic
capacitors have voltage dependence characteristics
and temperature dependence characteristics in
capacitance. So, the capacitance value may change
depending on the operating condition in the equipment.
Therefore, be sure to confirm the apparatus
performance of receiving influence in a capacitance
value change of a capacitor, such as leakage current
and noise suppression characteristics.
Moreover, check the surge-proof ability of a
capacitor in the equipment, if needed, because the
surge voltage may exceed specific value by the
inductance of the circuit.
C02E.pdf
09.9.18