GRM155R60J225ME15D Murata, GRM155R60J225ME15D Datasheet - Page 84

• Manufacturer Part Number: GRM155R60J225ME15D
• Manufacturer: Murata

Specifications of GRM155R60J225ME15D

• Tolerance (+ Or -): 20%
• Voltage: 6.3VDC
• Temp Coeff (dielectric): X5R
• Operating Temp Range: -55C to 85C
• Mounting Style: Surface Mount
• Construction: SMT Chip
• Case Style: Ceramic Chip
• Failure Rate: Not Required
• Wire Form: Not Required
• Product Length (mm): 1mm
• Product Depth (mm): 0.5mm
• Product Height (mm): 0.5mm
• Product Diameter (mm): Not Requiredmm
• Capacitance: 2.2uF
• Package / Case: 0402
• Lead Free Status / RoHS Status: Compliant

3
!Note
• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our
• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
sales representatives or product engineers before ordering.
!Note
82
No.
14
15
16
17
LLL/LLA/LLM Series Specifications and Test Methods (1)
LLL/LLA/LLM Series Specifications and Test Methods (1)
Continued from the preceding page.
Temperature
Cycle
Humidity
(Steady
Humidity
Load
High
Temperature
Load
State)
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
Item
Appearance
Capacitance
Change
D.F.
I.R.
Dielectric
Strength
Appearance
Capacitance
Change
D.F.
I.R.
Appearance
Capacitance
Change
D.F.
I.R.
Appearance
Capacitance
Change
D.F.
I.R.
No marking defects
Within T7.5%
W.V.: 25V min.; 0.025 max.
W.V.: 16V/10V max.; 0.035 max.
W.V.: 6.3V max.; 0.05 max.
More than 10,000MΩ or 500Ω · F (Whichever is smaller)
No failure
No marking defects
Within T12.5%
W.V.: 10V min.; 0.05 max.
W.V.: 6.3V max.; 0.075 max.
More than 1,000MΩ or 50Ω · F (Whichever is smaller)
No marking defects
Within T12.5%
W.V.: 10V min.; 0.05 max.
W.V.: 6.3V max.; 0.075 max.
More than 500MΩ or 25Ω · F
(Whichever is smaller)
No marking defects
Within T12.5%
W.V.: 10V min.; 0.05 max.
W.V.: 6.3V max.; 0.075 max.
More than 1,000MΩ or 50Ω · F
(Whichever is smaller)
In case Non "*" is added in PNs table, please refer to LLL/LLA/LLM Series Specifications and Test Methods (1).
In case "*" is added in PNs table, please refer to LLL/LLA/LLM Series Specifications and Test Methods (2).
Specifications
Fix the capacitor to the supporting jig in the same manner and
under the same conditions as (10).
Perform the five cycles according to the four heat treatments
listed in the following table. Let sit for 24T2 hours at room
temperature, then measure.
• Initial measurement.
Sit the capacitor at 40T2°C and 90 to 95% humidity for 500T12
hours. Remove and let sit for 24T2 hours at room temperature,
then measure.
Apply the rated voltage at 40T2°C and 90 to 95% humidity for
500T12 hours. Remove and let sit for 24T2 hours at room
temperature, then measure. The charge/discharge current is
less than 50mA.
Apply 200% of the rated voltage for 1000T12 hours at the
maximum operating temperature T3°C. Let sit for 24T2 hours
at room temperature, then measure. The charge/discharge
current is less than 50mA.
•Initial measurement.
Perform a heat treatment at 150
let sit for 24T2 hours at room temperature. Perform the initial
measurement.
Apply 200% of the rated DC voltage for one hour at the
maximum operating temperature T3°C. Remove and let sit for
24T2 hours at room temperature.
Perform initial measurement.
Temp. (°C)
Time (min.)
Step
Min. Operating
Temp.
30T3
1
+0
–3
Test Method
Temp.
Room
2 to 3
2
+0
–10
°C for one hour and then
Max. Operating
Temp.
30T3
3
+3
–0
Temp.
Room
2 to 3
4
C02E.pdf
09.9.18