GRM1885C1H101J Murata, GRM1885C1H101J Datasheet - Page 198

• Manufacturer Part Number: GRM1885C1H101J
• Manufacturer: Murata

Specifications of GRM1885C1H101J

• Capacitance: 100pF
• Tolerance (+ Or -): 5%
• Voltage: 50VDC
• Temp Coeff (dielectric): C0G
• Operating Temp Range: -55C to 125C
• Mounting Style: Surface Mount
• Package / Case: 0603
• Construction: SMT Chip
• Case Style: Ceramic Chip
• Failure Rate: Not Required
• Wire Form: Not Required
• Product Length (mm): 1.6mm
• Product Depth (mm): 0.8mm
• Product Height (mm): 0.8mm
• Product Diameter (mm): Not Requiredmm
• Dc: 07+
• Lead Free Status / Rohs Status: Compliant

18
!Note
• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our
• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
sales representatives or product engineers before ordering.
!Note
*1 "Room condition" Temperature: 15 to 35D, Relative humidity: 45 to 75%, Atmospheric pressure: 86 to 106kPa
*2 "C" expresses nominal capacitance value (pF).
196
No.
10
11
GA3 Series Specifications and Test Methods
1
2
3
4
5
6
7
8
9
Capacitance
Temperature
Characteristics
Operating
Temperature Range
Appearance
Dimensions
Dielectric Strength
Pulse Voltage
(Application: Type
GD/GF)
Insulation Resistance
(I.R.)
Capacitance
Dissipation
Factor (D.F.)
Q
Discharge
Test
(Application:
Adhesive Strength
of Termination
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
Type GC)
Item
Appearance
I.R.
Dielectric
Strength
Y55 to W125D
No defects or abnormalities
Within the specified dimensions
No defects or abnormalities
No self healing breakdowns or flash-overs have taken place in
the capacitor.
More than 6,000MΩ
Within the specified tolerance
Temperature characteristic guarantee is Y55 to W125D
Temperature characteristic guarantee is W20 to W85D
No defects or abnormalities
More than 1,000MΩ
In accordance with item No.4
No removal of the terminations or other defect should occur.
Char.
Char.
Char.
X7R
X7R
SL
SL
Temperature Coefficient
QU400W20C*
QU1000
W350 to Y1000ppm/D
Capacitance Change
Specification
Within T15%
D.F.V0.025
Specifications
2
(CU30pF)
(CF30pF)
Visual inspection
Using calipers
No failure should be observed when voltage in table is applied
between the terminations for 60T1 sec., provided the
charge/discharge current is less than 50mA.
10 impulse of alternating polarity is subjected.
(5 impulse for each polarity)
The interval between impulse is 60 sec.
Applied Voltage: 2.5kV zero to peak
The insulation resistance should be measured with DC500T50V
and within 60T5 sec. of charging.
The capacitance/Q/D.F. should be measured at a frequency of
1T0.2kHz (SL char.: 1T0.2MHz) and a voltage of
AC1T0.2V (r.m.s.)
The capacitance measurement should be made at each step
specified in Table.
SL char. :
The capacitance should be measured at even 85D between step
3 and step 4.
#Pretreatment for X7R char.
As in Fig., discharge is made 50 times at 5 sec. intervals from
the capacitor (Cd) charged at DC voltage of specified.
Solder the capacitor to the testing jig (glass epoxy board) shown
in Fig. 1.
Then apply 10N force in the direction of the arrow. The soldering
should be done using the reflow method and should be
conducted with care so that the soldering is uniform and free of
defects such as heat shock.
Perform a heat treatment at 150
let sit for 24T2 hrs. at room condition*
Type GB
Type GC/GD/GF
R1: 1,000Ω
Step
10kV
1
2
3
4
5
R3
Ct: Capacitor under test
V
R2: 100MΩ
Test Method
25T2 (20T2 for SL char.)
25T2 (20T2 for SL char.)
Max. Operating Temp.T2
25T2 (20T2 for SL char.)
Min. Operating Temp.T3
Fig. 1
Cd
Y
Continued on the following page.
Temperature (D)
W00
Y10
10N, 10T1s
Glass Epoxy Board
R3: Surge resistance
AC1500V (r.m.s.)
Test Voltage
D for 60T5 min. and then
1
.
Cd: 0.001µF
R1
DC1075V
Ct
R2
C02E.pdf
09.9.18